Assessment of Nickel and Chromium Release from Various Commercial Stainless-Steel Crowns (An In Vitro study)
Keywords:
Stainless Steel Crowns (SSCs), Nickel Release, Chromium Release, Artificial Saliva, Pediatric Dentistry, In Vitro Study, Metal Ion Release, Biocompatibility, Corrosion, Atomic Absorption SpectrophotometryAbstract
Prefabricated stainless steel crowns (SSCs) are one of the most common dental devices used to restore primary molars which are severely damaged or endodontically treated and as an abutment tooth for a space maintainer. The use of preformed crowns for primary tooth restoration reduces treatment time and number of visits to clinics. The chemical composition is 65–73% iron, 17–20% chromium, 8–13% nickel and less than 2% manganese, silicon and carbon.The frequent use of preformed crowns has led to concerns that heavy metals in the crowns could be released into the oral cavity and accumulate in the body. The purpose of this study was to determine how much nickel and chromium were released into artificial saliva by commercially available SSCs. Thirty samples of second primary lower molar SSCs were utilized, and they were split into three groups: group 1- Nichro SSC (China)-10 crowns, group 2-Kids crown (Korea)-10 crowns, group 3-3M™ ESPE™ SSCs (USA)-10 crowns. During the test, ten crowns from each group were placed in centrifuge tubes on a plastic platform. Using a flame-type atomic absorption spectrophotometer, the nickel and chromium levels of the artificial saliva samples taken within each tube following the removal of crowns and the control samples at the end of days 1, 7, 14, 21, and 28 were all determined. (GBC 932 plus, Australia). The amount of nickel and chromium released over a 28-day period across the three groups was estimated using two-way analysis of variance and pairwise comparison. The release of both nickel and chromium metal ions was observed in the three groups. However, there was no significant difference in the nickel and chromium release from SSCs among the three groups tested.
References
Kodaira H, Ohno K, Fukase N, Kuroda M, Adachi S, Kikuchi M, et al Release and systematic accumulation of heavy metals from preformed crowns used in the restoration of primary teeth J Oral Sci. 2013;55:161–56
Tiwari S, Bhayya D, Gupta S, Saxena S, Kathal S, Roy S. Effect of pH on nickel ion release from stainless steel crowns: AnIn Vitro Study Int Educ Res J. 2016;2:47–8
Akiyama M, Oshima H, Nakamura M. Genotoxicity of metals for dental use by chromosome aberration tests J Osaka Dent Univ. 2001;35:1–11
Grimaudo NJ. Biocompatibility of nickel and cobalt dental alloys Gen Dent. 2001;49:498–503
Huang TH, Ding SJ, Min Y, Kao C. Metal ion release from new and recycled stainless steel brackets Eur J Orthod. 2004;26:171–7
Pizzutelli S. Systematic nickel hypersensitivity and diet: Myth or reality? Eur Ann Allergy Clin Immunol. 2011;43:5–18
Gopikrishnan S, Melath A, Ajith VV, Mathews NB. A Comparative Study of biodegradation of various orthodontic archwires: AnIn Vitro Study J Int Oral Health. 2015;7:12–7
Bhaskar V, Subbareddy VV. Biodegradation of nickel and chromium from space maintainers: AnIn Vitro Study J Indian Soc Prevent Dent. 2010;28:6–12
Mohamed AA, Ahmed AM, Mahmoud TT. Comparison between nickel and chromium levels in saliva of children having space maintainers versus stainless steel crowns (Comparative Study) Int J Sci Res. 2016;5:663–6
Anand A, Sharma A, Kumar P, Sandhu M, Sachdeva S, Sachdev V. A comparative study of biodegradation of nickel and chromium from space maintainers: AnIn Vitro study Int J ClinPediatr Dent. 2015;8:37–41
Dos Santos AA, Pithon MM, Carlo FG, Carlo HL, de Lima BA, Dos Passos TA, et al Effect of time and pH on physical-chemical properties of orthodontic brackets and wires Angle Orthod. 2015;85:298–304
Elshahawuy W, Watanabe I. Biocompatibility of dental alloys used in dental fixed prosthodontics Tanta Dent J. 2014;11:150–9
Menek N, Basaram S, Karaman Y, Ceylan G, Tunc E. Investigation of nickel ion release from stainless steel crowns by square wave voltammetry Int J Electrochem Sci. 2012;7:6465–71
Park HY, Shearer TR. In vitro release of nickel and chromium from simulated orthodontic appliances Am J Orthod. 1983;84:156–9
Menne T, Brandup F, Thestrup-Pedersen K, Velien NK, Andersen JR, Yding F, et al Patch test reactivity to nickel alloys Contact Dermatitis. 1987;16:255–9
Matos de Souza R, Macedo de Menezes L. Nickel, chromium and iron levels in the saliva of patients with simulated fixed orthodontic appliances Angle Orthod. 2008;78:345–50
Barrett RD, Bishara SE, Quinio JK. Biodegradation of orthodontic appliances. Part I. Biodegradation of nickel and chromium In Vitro Am J Orthod Dentofac Orthop. 1993;103:8–14
Kulkarni P, Agrawal S, Bansal A. Jain A, Tiwari U, Anand A. Assessment of nickel release from various dental appliances used routinely in pediatric dentistry Indian J Dent. 2016;7:81–5
Syed M, Chopra R, Sachdev V. Allergic reactions to dental materials- A systematic review J Clin Diagn Res. 2015;9:4–9